DEscriptIONSDB10D is a kind of blend polyol used for pipe insulation system for city heating or cooling. When it combined with isocyanate(PM200) leads to the formation of rigid polyurethane foam by using PU injection foam equipment .The foam formed has the characteristics as following:
The thermal conductivity is low, which can meets the requirements of city heating and energy saving.
Service life of the foam is very long, over 30 years.
High temperature resistance and good dimensional stability of the foam, the highest temperature range is 140 ºC.
TYPICAL PHYSICAL PROPERTIES
importance: The above mentioned are typical test values, and the specific data may vary slightly due to environmental conditions.For our products, the data are not legally binding.
Other unmentioned matters and TDS&MSDS.Please visit our official website shundapu.en.made-in-china.com
Or please contact us for information:
Basic Info.
Model NO. SDB10D-Z01 Plastic Forming Method Injection Color Yellow Core Density ≥60 Kg/M3 Radial Compressive Strength ≥0.3MPa Initial Thermal Conductivity(50°c) ≤0.033W/(M•K) Close Cell Content ≥88% Water Absorption ≤10% Appearance Pale Yellow Liquid. Specific Gravity at 25°c 1.10±0.10 g/cm3 Viscosity at 25°c 300±100 Cps Shelf Life 12 Months Trademark shunda Transport Package Iron Drum Specification 200kg Origin China HS Code 39072090Product Description
Customer Question & Answer Ask something for more details
DEscriptIONSDB10D is a kind of blend polyol used for pipe insulation system for city heating or cooling. When it combined with isocyanate(PM200) leads to the formation of rigid polyurethane foam by using PU injection foam equipment .The foam formed has the characteristics as following:
- The thermal conductivity is low, which can meets the requirements of city heating and energy saving.
- Service life of the foam is very long, over 30 years.
- High temperature resistance and good dimensional stability of the foam, the highest temperature range is 140 ºC.
| Physical Properities | Test Method | Metric | Value |
| Core Density | GB/T 6343-2009 | kg/m3 | ≥60 |
| Radial Compressive Strength | GB/T 8813-2008 | MPa | ≥0.3 |
| Initial Thermal Conductivity(50°C) | GB/T 10294-2008 | W/(m·K) | ≤0.033 |
| Close Cell Content | GB/T 10799-2008 | % | ≥88 |
| Water Absorption | GB/T 8810-2005 | % | ≤10 |
| Air bubbles | GB/T 29047 | mm | 1/3Insulation thickness. |
| Average cell size. | GB/T 29047 | mm | ≤0.5 |